Bison Coated George Moate Rotary Blade LH 210x70x12mm

Bison Coated George Moate Rotary Blade LH

210x70x12mm

50mm Bolt Hole Centre

Hole 22mm

A special wear-resistant alloy is used to coat our Bison Coated wearing parts. The carrier material used is an alloy
with a high chromium content, to which tungsten carbide particles have been added.

The coating process takes place at extremely high temperatures in a controlled atmosphere.
The almost perfect cohesion between the coating and the body ensures maximum resistance and durability.

The coating is characterised by its compactness and its homogeneous surface.
The average hardness is around 600 HV with a carbide hardness between 2500 and 3000 HV.

The coating process used ensures excellent anchoring of the coating to the body.
Complete or partial detachment of the coating is almost impossible, even as a result of impacts caused by stones in the ground.

The coating not only extends the service life of the tool, but also ensures high dimensional stability as a result of the low wear, which is essential for a consistently good work result.